LASCOD/ITALY

Alginates

Wide range of alginates, with or without color change, for high precision dental impressions.

All Lascod alginates maintain a very high dimensional stability over time (up to 168 hours) if properly stored, maintaining the high precision and elasticity unchanged.

The chromatic phase indicator helps the preparation of the impression regardless of the environmental conditions, the temperature and hardness of the water used.

The pleasant aromas (mint, spearmint, strawberry, mango) minimize salivation and the emetic reflex.

Kromopan

Since Kromopan was created it has been an incredible break through in dentistry, allowing, thanks to the chromatic phase indicator (purple: mixing -> pink: tray loading -> white: insertion in mouth), the impression taking with high quality and easy check through the working phases.

Available also in the single-dose version, for an easier and faster use, and in the “type 2” version, with a longer working time.

Plasters

Lascod plasters are formulated to give an optimal combination of quality, ease of use and time saving. The finely micronized powder allows the perfect reproduction of the details. The physical properties allow the creation of precise models enhancing the prosthetic product. Extraordinary consistency and surface hardness, guarantee resistant margins even in thin thicknesses, no risk of breakage or chipping during the cutting, finishing and extraction phases from the impression materials. The hermetic closure of the packaging guarantees long product storage times while keeping its characteristics unchanged.

Study models, master models, removable dies for bridges and crowns, implant prostheses, antagonists, are just some of the dental models that can be made with Lascod stones.

Thanks to the experience gained with color changing alginates (first of all Kromopan) Lascod has patented Kromotypo 3 and Kromotypo 4, the first dental plasters with chromatic phases indicator, the color change helps the preparation of the model regardless of environmental conditions, temperature and water hardness.

Ortotypo4

Type 4 extra-hard stone specifically developed for all orthodontic models, demonstration and antagonis

Characterized by high hardness, extra fine granulometry, low expansion and fast setting time.
Ortotypo4 is often used with acrylic resins (both hot or cold polymerization processes) with unaltered surface and no models’ breakage risks .
It is compatible with all impression material and all products for the isolation of plaster against plaster.
Final color: Brilliant white.

• Water/powder ratio: 22 ml/100 g
• Imbibition time: 20’’
• Manual mixing time: 60’’
• Mechanical mixing time: 30’’
• Pouring time: 3’
• Setting time: 7’
• Time for separation after setting*: 30’
• Setting expansion (after 2 hours): 0,08%
• Compressive strength (after 24 hours): 103 MPa – 14.927 Psi – 1.051 Kg/cm2
• Rockwell hardness (after 24 hours): 95 HRl

Measurements at 23°C with deionized water.

* Depending on the impression material used, the times indicated may vary.

PACKAGING

TOR425 – 1 x 25 kg bucket
TOR412 – Box containing 10 x 1.250 kg bags (12.5 kg)

Modeltypo

Type 4 extra hard stone, Modeltypo is a specific product for the preparation of master models for removable prosthesis, implant-supported dentures with or without metal frameworks and antagonist models.

The product final hardness, low expansion setting, smooth and detailed surface are a guarantee for the creation of an accurate prosthesis.
Compatible with all impression material and all products for the isolation of plaster against plaster.
Color: Pink.

• Water/powder ratio: 25 ml/100 g
• Imbibition time: 20’’
• Manual mixing time: 60’’
• Mechanical mixing time: 30’’
• Pouring time: 3’
• Setting time: 7’
• Time for separation after setting*: 30’
• Setting expansion (after 2 hours): 0,08%
• Compressive strength (after 24 hours): 70 MPa – 10.144 Psi – 713 Kg/cm²
• Rockwell hardness (after 24 hours): 75 HRl

Measurements at 23°C with deionized water.

* Depending on the impression material used, the times indicated may vary.

PACKAGING

TPM425 – 1 x 25 kg bucket
TPM412 – Box containing 10 x 1.250 kg bags (12.5 kg)

Singletypo4 golden brown

Type 4 extra hard stone specific for the preparation of total and partial non-removable master models, stumps preparation, metal framework, implants and antagonist models.

Additionally, physical properties and specific color are ideal for all CAD-CAM reading techniques.

The innovative formula, low expansion setting, high thixotropicity, excellent fluidity, optimal working time, resistance to compression and abrasion are a guarantee for obtaining accurate, fine, homogeneous and chippings free models with smooth surfaces.
Singletypo4 is compatible with all impression material and all products for the isolation of plaster against plaster.
Final color: Golden brown.

• Water/powder ratio: 20 ml/100 g
• Imbibition time: 20”
• Manual mixing time: 60”
• Mechanical mixing time: 30”
• Pouring time: 3’
• Setting time: 7’Time for separation after setting*: 30’
• Setting expansion (after 2 hours): 0,08%
• Compressive strength (after 24 hours): 84 MPa – 12.174 Psi – 860 Kg/cm²
• Rockwell hardness (after 24 hours): 90 HRl

Measurements at 23°C with deionized water.

* Depending on the impression material used, the times indicated may vary.

PACKAGING

TXE425 – 1 x 25 kg bucket
TXE406 – 1 x 6 kg bucket
TXE412 – Box containing 10 x 1.250 kg bags (12.5 kg)